Hot Rolled Mild Steel PLates
Prime, annealed and pickled Mild Steel Plates are produced after Hot rolling of Mild Steel Slabs.
Prime, annealed and pickled Mild Steel Plates are produced after Hot rolling of Mild Steel Slabs.
| Grade | : | IS 2062/1999-A-B-C. SAILMA-300 300HI 350 350HI 410 410HI 450 450HI. ASTM-A-36,DIN 17100-ST 52.3 |
| Thickness | : | 6 to 150 mm |
| Width | : | Upto 2500 mm |
| Length | : | Cut into desired lengths |
| Cut | : | Shear Cut |
DOWNLOAD PDF
Manufacturing Range
Dimensional Tolerance
Surface Finish and Condition
Chemical Composition
Mechanical Properties
Manufacturing Range
| Product | Thickness(mm) | Width (mm) | Length(mm) | Surface Finish | Edge Condition |
|---|---|---|---|---|---|
| Hot Rolled Plate | 6 to 150mm | 850-2000 mm | Upto 16000 mm | Hot Rolled | Sheared/Mill Edge |
Dimensional Tolerance
| Product | Thickness Tolerance | Length Tolerance | Width Tolerance |
|---|---|---|---|
| Hot Rolled Black | +0.50/-0.25 for 5 to 10mm +0.75/-0.25 for 10 to 25mm +1.0/-0.25 for 25 to 40mm +1.5/-0.25 for Above 40mm |
+30/0 mm(Mill Edge) +10/-0 mm (Trim Edge) |
+100/-0 mm (Mill Edge) +20/-0 mm(Trim Edge) |
Surface Finish and Condition
| ASTM A 480/BS 1449 Part 2 | DIN 17 400 | Description | Surface Condition |
|---|---|---|---|
| No.0 Finish/HR Black | I c or b | Hot Rolled | Layer of Mill Scale |
| No.1 Finish | II a or c1 II a or c2 |
Hot rolled annealed and pickled | Mechanically and Chemically Clean |
Chemical Composition
| Specification | Grade | %C | %Mn | %P | %S | %Si | %CE | %Nb+V+Ti | AI% | ||||||||
| Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | ||
| IS 2062/1999 | A | - | 0.23 | - | 1.50 | - | 0.050 | - | 0.050 | - | 0.40 | - | 0.42 | - | - | - | - |
| B | - | 0.22 | - | 1.50 | - | 0.045 | - | 0.045 | - | 0.40 | - | 0.41 | - | - | - | - | |
| C | - | 0.20 | - | 1.50 | - | 0.040 | - | 0.040 | - | 0.40 | - | 0.39 | - | - | - | - | |
| Mode of deoxidation : Grade A - Killed or Semi Killed. Grade B and C - Killed. Cu Between 0.2 and 0.35% for copper bearing quality |
|||||||||||||||||
| SAILMA | 300 | - | 0.25 | - | 1.50 | - | 0.055 | - | 0.055 | - | - | - | - | 0.30 | - | - | |
| 300 HI | - | 0.20 | - | 1.50 | - | 0.040 | - | 0.040 | - | - | - | - | 0.30 | - | - | ||
| 350 | - | 0.25 | - | 1.50 | - | 0.055 | - | 0.055 | - | - | - | - | 0.30 | - | - | ||
| 350HI | - | 0.20 | - | 1.50 | - | 0.040 | - | 0.040 | - | - | - | - | 0.30 | - | - | ||
| 410 | - | 0.25 | - | 1.50 | - | 0.055 | - | 0.055 | - | - | - | - | 0.30 | - | - | ||
| 410 HI | - | 0.20 | - | 1.50 | - | 0.040 | - | 0.040 | - | - | - | - | 0.30 | - | - | ||
| 450 | - | 0.25 | - | 1.50 | - | 0.055 | - | 0.055 | - | - | - | - | 0.30 | - | - | ||
| 450 HI | - | 0.20 | - | 1.50 | - | 0.040 | - | 0.040 | - | - | - | - | 0.30 | - | - | ||
| ASTM-A-36 | - | 0.25 | 0.80 | 1.20 | - | 0.040 | - | 0.050 | 0.15 | 0.40 | - | - | - | - | - | - | |
| DIN 17100 | ST 52.3 | 0.20 | 0.22 | - | 1.60 | - | 0.040 | - | 0.040 | - | 0.55 | - | - | - | - | 0.02 | - |
Mechanical Properties
| Specification | Grade | Yield Strength Mpa Min |
Ultimate Tensile Strength Mpa Min |
Elongation % Min GL 5.65 / S0 |
||
| < 20 | 20-40 | > 40 | ||||
| IS 2062/1999 | A | 250 | 240 | 230 | 410 | 23 |
| B | 250 | 240 | 230 | 410 | 23 | |
| C | 250 | 240 | 230 | 410 | 23 | |
| SAILMA | 300 | 300 | 440-560 | 20 | ||
| 300 HI | 300 | 440-560 | 21 | |||
| 350 | 350 | 490-610 | 20 | |||
| 350 HI | 350 | 490-610 | 21 | |||
| 410 | 410 | 540-660 | 19 | |||
| 410 HI | 410 | 540-660 | 20 | |||
| 450 | 450 | 570-720 | 18 | |||
| 450 HI | 450 | 570-720 | 19 | |||
| ASTM-A-36 | 250 | 400-550 | 200mm-18, 20mm-21 |
|||
| DIN 17100 | ST 52.3 | 0 16mm | >16 0 40 | >40 0 63 | 490-630 | 18 |
Hot Rolled Stainless Steel Plates
Prime, annealed and pickled Stainless Steel plates are produced after hot rolling of Staibnless Steel Slabs.We offer Plasma edge cutting for 90 degree sharp cuts.
Prime, annealed and pickled Stainless Steel plates are produced after hot rolling of Staibnless Steel Slabs.We offer Plasma edge cutting for 90 degree sharp cuts.
| Grade | : | AISI 201, AISI 202, AISI 204, AISI 301, AISI 303, AISI 304, AISI 304L, AISI 310. AISI 316, AISI 316L, AISI 321. SIL 1(1% Nickel Max), SIL 4 (4% Nickel Max) |
| Thickness | : | 8 to 50 mm |
| Width | : | Upto 2500 mm |
| Length | : | Cut into desired lengths |
| Cut | : | Shear Cut |
Manufacturing Range
| Product | Thickness(mm) | Width (mm) | Length(mm) | Surface Finish | Edge Condition |
|---|---|---|---|---|---|
| Hot Rolled Plate | 8 to 50mm | 1000-1500 mm | Upto 8000 mm | Hot Rolled Annealed and Pickled | Sheared/Mill Edge |
Dimensional Tolerance
| Hot Rolled Black and Hot Rolled Annealed and Pickled Plate | ||
| +0.50/-0.25 for 5 to 10 mm | ||
| +0.75/-0.25 for 10 to 25 mm | +30/-0 mm (Mill Edge) | +100/-0 mm(Mill Edge) |
| +1.0/-0.25 for 25 to 40mm | +10/-0 mm (Trim Edge) | +20/-0 mm(Trim Edge) |
| +1.5/-0.25 for Above 40mm |
Surface Finish and Condition
| ASTM a 480/BS 1449 Part 2 | DIN 17 400 | Description | Surface Condition |
|---|---|---|---|
| No. 0 Finish/ HR Black | I c or b | Hot Rolled | Layer of Mill Scale |
| No. 1 Finish | II a or c1 II a or c2 |
Hot Rolled annealed and pickled | Mechanically and chemically clean |
Chemical Compositin
| AISI - ASTM Grade |
%C Max |
%Mn Max |
%Si Max |
%P Max |
%S Max |
% Cr | % Ni | % Mo | % N Max |
% Cu Max |
% Others |
| 201 | 0.15 | 5.5 - 7.S | 1.00 | 0.06 | 0.03 | 16.0 - 18.0 | 3.5 - 5.5 | - | 0.25 | - | - |
| 202 | 0.15 | 7.5-10.0 | 1.00 | 0.06 | 0.03 | 17.0-19.0 | /1.0-6.0 | - | 0.25 | - | - |
| 301 | 0.15 | 2.00 | 1.00 | 0.045 | 0.030 | 16.00-18.00 | 6.00-8.00 | - | 0.10 | - | - |
| 304 | 0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 18.00-20.00 | 8.00-10.50 | - | 0.10 | - | - |
| 304L | 0.03 | 2.00 | 0.75 | 0.045 | 0.030 | 18.00-20.00 | 8.00-12.00 | - | 0.10 | - | - |
| 304LN | 0.03 | 2.00 | 0.75 | 0.045 | 0.030 | 18.00-20.00 | 8.00-12.00 | - | 0.10-0.16 | - | - |
| 3105 | 0.08 | 2.00 | 1.50 | 0.045 | 0.030 | 24.00-26.00 | 19.00-22.00 | - | - | - | >- |
| 316 | 0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10 | - | - |
| 316L | 0.03 | 2.00 | 0.75 | 0.045 | 0.030 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10 | - | - |
| 316 LN | 0.03 | 2.00 | 0.75 | 0.0115 | 0.030 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10-0.16 | - | |
| 316 Ti | 0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 16.00-18.00 | 10,00-14.00 | 2.00-3.00 | 0.10 | - | Ti=S(C+N)Min./0.70 Max. |
| 321 | 0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.00-19.00 | 9.00-12.00 | - | 0.10 | - | Cb=10X (%C Min.)/1.00 Max. |
| 347 | 0.08 | 2.00 | 0.75 | 0.0/45 | 0.030 | 17.00-19.00 | 9.00-13.00 | - | - | Ti=6X(C+N)Min./-0.75 Max. | |
| 410 | 0.15 | 1.00 | 1.00 | 0.040 | 0.030 | 11.50-13.50 | 0.75max | - | - | - | - |
| 4105 | 0.08 | 1.00 | 1.00 | 0.0/40 | 0.030 | 11.50-13.50 | 0.60max | - | - | - | - |
| 430 | 0.12 | 1.00 | 1.00 | 0.040 | 0.030 | 16.00-18.00 | 0.75max | - | - | - | - |
| 420 | 0.15min | 1.00 | 1.00 | 0.040 | 0.030 | 12.00-14.00 | 0.75max | - | - | Mo=0.50 Max |
Mechanical Properties
| AISI Grade | TensileStrength Mpa(Min.) |
YieldStrength Mpa(Min.) |
Elongation %(Min.) |
Hardness BHN(Max) |
Hardness RB(Max) |
| 213 | 515 | 275 | 40 | - | - |
| 202 | 515 | 205 | 40 | - | - |
| 33 | 515 | 205 | 40 | 217 | 95 |
| 334 | 515 | 205 | 40 | 201 | 92 |
| 304L | 485 | 170 | 40 | 201 | 92 |
| 3134LN | 515 | 205 | 40 | 201 | 92 |
| 3135 | 515 | 205 | 40 | 217 | 95 |
| 36 | 515 | 205 | 40 | 217 | 95 |
| 36L | 485 | 170 | 40 | 217 | 95 |
| 316 LN | 515 | 205 | 40 | 217 | 95 |
| 316 Ti | 515 | 205 | 35 | 217 | 95 |
| 321 | 515 | 205 | 40 | 217 | 95 |
| 347 | 515 | 205 | 40 | 201 | 92 |
| 410 | 450 | 205 | 20 | 217 | 96 |
| 4105 | 415 | 205 | 22 | 183 | 89 |
| 430 | 415 | 205 | 22 | 183 | 89 |
| 420 | 690 | - | 15 | 217 | 96 |
Equivalent Specification
| Grade | IS India | AISI USA | DIN Germany | AFNOR France | JIS Japan | BS Britain | SIS Sweden |
| SS 301 | X 10 Cr 17 Ni 7 | 301 | 1.4310 | Z 12 CN 17-08 | SUS 301 | 301 S 21 | 142331 |
| SS 304 | X 02 Cr 19 Ni 10 | 304 | 1.4301 | Z 6 CN 18-19 | SUS 304 | 304 S 15 | 142333 |
| SS 304L | - | 304 L | 1.4306 | Z 2CN 18-10 | SUS 304 L | 304 S 11 | 142352 |
| 310S | - | 310 S | 1.4845 | - | SUS 310 S | - | 142361 |
| SS 316 | X04 Cr 17 Ni 12 Mo 2 | 316 | 1.4401 1.4436 |
Z6 CND 17-11 | SUS 316 | 316 S 31 | 142347 142343 |
| 56361L | X02 Cr 17 Ni 12 Mo 2 | 316 L | 1.4404 1.4435 |
Z 2 CND 17-12 Z 2 CND 17-13 |
SUS 316 L | 316 S 31 | 142338 142353 |
| 55321 | X04 Cr 18 Ni 10 Ti 20 | 321 | 1.4878 | Z 6 CNT 18-12 | SUS 321 | 321 S 31 | 142337 |
| SS 409 | - | 409 | 1.4512 | Z 5 CT 12 | SUS 409 | 409 S 17 | - |
| SS 410S | - | 410 S | - | - | - | - | - |
| SS 430 | X 07 Cr 17 | 430 | 1.4016 | Z 8 C 17 | SUS 430 | 430 S 17 | 142320 |
| SS 409M | - | 1.4003 | - | - | HYFAB3/12 | - |
| Grade | UNS | UNI Italy |
| SS301 | S 30100 | X 12 Cr Ni 1707 |
| SS304 | S 30400 | X 5 Cr Ni 1810 |
| SS 304L | S 30303 | X 2 cR nI 1811 |
| SS 310S | S 31008 | X 6 Cr Ni 2520 |
| SS 316 | S 31600 | X 8 Cr nI Mo 1713 |
| SS 316L | S 31603 | X 2 Cr Ni Mo 1712 X 2 Cr Ni Mo 1713 |
| SS 321 | S 32100 | X 6 Cr Ni Ti 1811 |
| SS 409 | S 40900 | - |
| SS 4105 | - | - |
| SS 430 | S 43000 | X 12 Cr 17 C |
| SS 409M | - | - |
Hot Rolled Alloy Steel Plates
Prime, annealed and pickled Alloy Steel plates are produced after hot rolling of Alloy Steel Slabs. We offer Plasma edge cutting for 90 degree sharp cuts.
Prime, annealed and pickled Alloy Steel plates are produced after hot rolling of Alloy Steel Slabs. We offer Plasma edge cutting for 90 degree sharp cuts.
| Grade | : | IS 2002/1992 -1-2-3, ASTM-A 515 M-60-65-70,ASTM-A516 M-60-65-70. IS 6240/1999. JIS G 4051-S45C,EN10025- S257 JR-5275 JO-S355 JR-S355 JO. BS 970-EN45-EN 8-EN 9-EN 16-EN 19, DIN 17100-C-35-C-45-C-55. DIN 17210-16MnCR5-20MnCR5, SAE 1970-8620. |
| Thickness | : | 6 to 150 mm |
| Width | : | Upto 2500 mm |
| Length | : | Cut into desired lengths |
| Cut | : | Shear Cut |
Manufacturing Range
| Product | Thickness(mm) | Width (mm) | Length(mm) | Surface Finish | Edge Condition |
|---|---|---|---|---|---|
| Hot Rolled Plate | 6 to 120mm | 1000-2500 mm | Upto 16000 mm | Hot Rolled Annealed and Pickled | Sheared/Mill Edge |
Dimensional Tolerance
| Product | Thickness Tolerance | Length Tolerance | Width Tolerance |
|---|---|---|---|
| Hot Rolled Black | +0.50/-0.25 for 5 to 10mm +0.75/-0.25 for 10 to 25mm +1.0/-0.25 for 25 to 40mm +1.5/-0.25 for Above 40mm |
+30/-0 mm(Mill Edge) +10/-0 mm (Trim Edge) |
+100/-0 mm (Mill Edge) +20/-0 mm(Trim Edge) |
Surface Finish and Condition
| ASTM A 480/BS 1449 Part 2 | DIN 17 400 | Description | Surface Condition |
|---|---|---|---|
| No.0 Finish/HR Black | I c or b | Hot Rolled | Layer of Mill Scale |
| No.1 Finish | II a or c1 II a or c2 |
Hot rolled annealed and pickled | Mechanically and Chemically Clean |
Chemical Composition
| Specification | Grade | %C | %Mn | %P | %S | %Si | %CE | ||||||
| Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | ||
| IS 2002/1991 | 1 | - | 0.18 | 0.5 | 1.2 | - | 0.035 | - | 0.04 | 0.15 | 0.35 | - | 0.44 |
| 2 | - | 0.2 | 0.5 | 1.2 | - | 0.035 | - | 0.04 | 0.15 | 0.35 | - | 0.44 | |
| 3 | - | 0.22 | 0.5 | 1.2 | - | 0.035 | - | 0.04 | 0.15 | 0.35 | - | 0.44 | |
| ASTM-A 515 M |
60 | 0.24 | 0.27 | - | 0.9 | - | 0.035 | - | 0.035 | 0.15 | 0.4 | - | - |
| 65 | 0.28 | 0.31 | - | 0.9 | - | 0.035 | - | 0.035 | 0.15 | 0.4 | - | - | |
| 70 | 0.31 | 0.33 | - | 1.2 | - | 0.035 | - | 0.035 | 0.15 | 0.4 | - | - | |
| ASTM-A 516 M |
60 | 0.21 | 0.23 | TH 12.5 and below- .60 - .90 |
For TH above 12.5-.60 - .90 |
- | 0.035 | - | 0.035 | 0.15 | 0.4 | - | - |
| - | 0.9 | - | 0.035 | - | 0.035 | 0.15 | 0.4 | - | - | ||||
| 65 | 0.24 | 0.26 | 0.85 | 1.2 | - | 0.035 | - | 0.035 | 0.15 | 0.4 | - | - | |
| 70 | 0.27 | 0.28 | 0.85 | 1.2 | - | 0.035 | - | 0.035 | 0.15 | 0.4 | - | - | |
| IS 6240/1999 | - | - | 0.16 | 0.3 | - | - | 0.3 | - | 0.03 | - | 0.25 | - | - |
| JIS G 4501 | S45C | 0.42 | 0.48 | 0.6 | 0.9 | - | 0.03 | - | 0.0.4 | - | - | - | - |
| EN10025 | S275 JR | - | 0.21 | - | 1.5 | - | 0.045 | - | 0.05 | - | - | - | 0.42 |
| S275 JO | - | 0.21 | - | 1.5 | - | 0.04 | - | 0.04 | - | - | - | 0.42 | |
| S355 JR | - | 0.24 | - | 1.6 | - | 0.045 | - | 0.05 | - | 0.55 | - | 0.47 | |
| S355 JO | - | 0.24 | - | 1.6 | - | 0.04 | - | 0.04 | - | 0.55 | - | 0.47 | |
| BS 970 | EN45 | 0.5 | 0.6 | 0.7 | 1 | - | 0.05 | - | 0.05 | 1.5 | 2 | - | - |
| EN 8 | 0.35 | 0.45 | 0.6 | 1 | - | 0.06 | - | 0.06 | 0.05 | 0.35 | - | - | |
| EN 9 | 0.5 | 0.6 | 0.5 | 0.8 | - | 0.06 | - | 0.06 | 0.05 | 0.35 | - | - | |
| EN 16 | 0.3 | 0.4 | 1.3 | 1.8 | - | 0.05 | - | 0.05 | 0.1 | 0.35 | - | - | |
| EN 19 | 0.35 | 0.45 | 0.5 | 0.8 | - | 0.05 | - | 0.05 | 0.1 | 0.35 | - | - | |
| DIN 17100 | C-35 | 0.32 | 0.39 | 0.5 | 0.8 | - | 0.045 | - | 0.05 | 0.15 | 0.35 | - | - |
| C-45 | 0.42 | 0.5 | 0.5 | 0.8 | - | 0.045 | - | 0.05 | 0.15 | 0.35 | - | - | |
| C-55 | 0.52 | 0.6 | 0.6 | 0.8 | - | 0.045 | - | 0.05 | 0.15 | 0.35 | - | - | |
| DIN 17210 | 16MnCr5 | 0.14 | 0.19 | 1 | 1.3 | - | 0.035 | - | 0.04 | 0.15 | 0.4 | - | - |
| 20MnCr5 | 0.17 | 0.22 | 1.1 | 1.4 | - | 0.035 | - | 0.04 | 0.15 | 0.4 | - | - | |
| SAE 1970 | 8620 | 0.18 | 0.23 | 0.7 | 0.9 | - | 0.04 | - | 0.04 | 0.15 | 0.3 | - | - |
Loreum Ipsum
| Specification | Grade | AI% | Cu% | Mo% | Cr% | Ni% | |||||
| Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | ||
| IS 2002/1992 | 1 | - | 0.022 | - | 0.1 | - | - | - | - | 0.15 | - |
| 2 | - | 0.022 | - | 0.1 | - | - | - | - | 0.15 | - | |
| 3 | - | 0.022 | - | 0.1 | - | - | - | - | 0.15 | - | |
| ASTM-A 515 M | 60 | - | 0.02 | - | 0.02 | - | - | - | - | 0.15 | - |
| 65 | - | 0.02 | - | 0.02 | - | - | - | - | 0.15 | - | |
| 70 | - | 0.02 | - | 0.02 | - | - | - | - | 0.15 | - | |
| ASTM-A 516 M | 60 | - | 0.02 | - | - | - | - | - | - | - | - |
| 65 | - | 0.02 | - | - | - | - | - | - | - | - | |
| 70 | - | 0.02 | 0.02 | - | - | - | - | - | - | - | |
| IS 6240/1999 | - | - | 0.02 | - | - | - | - | - | - | - | - |
| BS 970 | EN 16 | - | - | - | - | 0.2 | 0.35 | - | - | - | - |
| EN 19 | - | - | - | - | 0.2 | 0.4 | 0.9 | 1.5 | - | - | |
| DIN 17210 | 16MnCr5 | - | - | - | - | - | - | 0.8 | 1.1 | - | - |
| 20MnCr5 | - | - | - | - | - | - | 1 | 1.3 | - | - | |
| SAE 1970 | 8620 | - | - | - | - | 0.15 | 0.25 | 0.4 | 0.6 | 0.4 | 0.7 |
Mechanical Properties
| Specification | Grade | Yield Strength Mpa Min | Ultimite Tensile Strength Mpa Min |
Elongation % Min GL 5.65 / S0 |
|||
| < 20 | 20 - 40 | > 40 | |||||
| IS 2002/1992 | 1 | 235 | 225 | 215 | 360- 480 | 24 | |
| 2 | 265 | 255 | 245 | 410 - 530 | 22 | ||
| 3 | 290 | 285 | 280 | 460 - 580 | 21 | ||
| 200 mm | 50 mm | ||||||
| ASTM - A 515 M | 60 | 220 | 415-550 | 21 | 25 | ||
| 65 | 240 | 450-585 | 19 | 23 | |||
| 70 | 260 | 485-620 | 17 | 21 | |||
| ASTM - A 516 M | 60 | 220 | 145-550 | 21 | 25 | ||
| 65 | 240 | 450-585 | 19 | 23 | |||
| 70 | 260 | 485-620 | 17 | 21 | |||
| IS 6240/1999 | 240 | 350-450 | 25 | ||||
| JIS G 4051 | S45C | ||||||
| EN10025 | S275 JR | 235 | 410-560 | 22 | |||
| S275 JO | 235 | 410-560 | 20 | ||||
| S355 JR | 315 | 490-630 | 22 | ||||
| S355 JO | 315 | 490-630 | 20 | ||||
| BS 970 | EN 45 | As per Contractual obligition | |||||
| EN 8 | 40-50 | 22 | |||||
| EN 9 | 45-55 | 18 | |||||
| EN 16 | 45-55 | 22 | |||||
| EN 19 | 50-60 | 22 | |||||
| DIN 17100 | C - 35 | 33 | 55-70 | 20 | |||
| C - 45 | 38 | 63-78 | 17 | ||||
| C - 55 | 43 | 71-86 | 15 | ||||
| DIN 17210 | 16MnCr5 | 65 | 90-120 | 9 | |||
| 20MnCr5 | 75 | 110-140 | 7 | ||||
| SAE 1970 | 8620 | ||||||